Chinese steel foundries produce AISI 1026 SAE UNS G10260 carbon steel castings. Today, we will introduce the chemical composition, physical and mechanical properties and equivalent material grades of AISI 1026. The following sections will give you an overview of AISI 1026 carbon steel in details.
The chemical composition of AISI 1026 carbon steel is outlined in the following table.
|Sulfur, S||≤ 0.050|
|Phosphorous, P||≤ 0.040|
The following table shows the physical properties of AISI 1026 carbon steel.
|Density||7.858 g/ cm3||0.2839 lb/in³|
The mechanical properties of cold drawn AISI 1026 carbon steel are displayed in the following table.
|Tensile strength||490 MPa||71100 psi|
|Yield strength||415 MPa||60200 psi|
|Bulk modulus (typical for steel)||140 GPa||20300 ksi|
|Shear modulus (typical for steel)||80.0 GPa||11600 ksi|
|Elastic modulus||190-210 GPa||27557-30458 ksi|
|Elongation at break (In 50 mm)||15.00%||15.00%|
|Reduction of area||40.00%||40.00%|
|Hardness, Knoop (converted from Brinell hardness)||163||163|
|Hardness, Rockwell B (converted from Brinell hardness)||78||78|
|Hardness, Vickers (converted from Brinell hardness)||149||149|
|Machinability (based on AISI 1212 steel as 100 machinability. The machinability of Group I bar, rod, and wire products can be improved by cold drawing.)||75||75|
The thermal properties of AISI 1026 carbon steel are given in the following table.
|Thermal expansion co-efficient (@0.000-100°C/32-212°F)||12.1 µm/m°C||6.72 µin/in°F|
|Thermal conductivity (0ºC)||51.9 W/mK||360 BTU in/hr.ft².°F|
Equivalent materials to AISI 1026 carbon steel are given in the following table.
|ASTM A29||ASTM A510||ASTM A512||ASTM A513||ASTM A519|
|ASTM A545||ASTM A576||ASTM A830||MIL F-20670||MIL S-22698|
|MIL S-24093||SAE J1397||SAE J403||SAE J412||SAE J414|
Yide casting is an experienced casting foundry, specialized in casting iron for 28years, can manufacture the casting iron parts according to your drawing file and requirement. If you are looking for a casting manufacturer, please feel free to contact us for more details, and you are welcome to visit our factory for more details.
Cast Steel Excavator Bucket Teeth
Bucket teeth are the most important consumable parts on excavators. Excavator bucket teeth are composed of prong and holder, and connected by a pin shaft, which is similar to human teeth. The process of cast steel excavator bucket teeth mainly includes sand casting and precision casting.
Cast Steel Investment Automobile Parts
Yide casting produces the casting parts with JM mark, produce qualified best casting parts for you, sample first, production after deposit. The auto parts produced by Yide Casting adopt precision investment casting technology. All products support non-standard customization with drawings and reliable quality.
Lost Wax Steel Investment Castings with CNC Machining
Yide casting has a steel casting partner to manufacture cast steel parts, and finish the automobile spare steel casting parts after CNC Machining from Yide casting. This Steel casting part is made of steel material, the weight of this steel casting part is about 0.02-50kg.